Professional China Monocrystal Diamond Lapping Powder - FCCS07 FeCuCoSn Pre Alloyed Metal Powde for Medium to High Quality Diamond Tools – SinoDiam

FCCS07 FeCuCoSn Pre Alloyed Metal Powde for Medium to High Quality Diamond Tools

1. What is Pre-alloyed Powder

Pre-alloyed powders are harder, less compressible and hence require higher pressing loads to produce high density compacts. However, they are capable of producing high strength sintered materials. Pre-alloying is also used when the production of a homogeneous material from elemental powders requires very high temperatures and long sintering times. The best examples are the stainless steels, whose chromium and nickel contents have to be pre-alloyed to allow economic production by powder metallurgy.

2. The Parameters of FCCS07

	Main Element	Fe, Cu, Co, Sn
	Theoretical Density	7.84g/cm³
	Sintering Temperature	790℃
	Bending Strength	1500Mpa
	Hardness	105-110HRB

3. FCCS07 Pre-alloyed Powder Character

• The powder has good wetting ability to the diamond and great mechanical granulating to other metal powders, it can help the products achieve a great value on speed and life.  
• Applied to medium to high quality granite diamond blade, ceramic diamond blade, diamond wire and diamond core bits

4. Usage Instruction for Ceramic Cutting Blade

1. Metal Powder

• 30-50% FCCS07
• + 25-35% Cu
• + 3-6% Sn
• +2-5% Ni
• +7-10% CUCS
• + Fe for the balance

    B. Diamond for Dry Cutting Ceramic 

• 50/60 @ 30%
• 60/70 @ 40%
• 70/80 @30%
• Diamond Concentration @ 13-15%

    C. Diamond for Wet Cutting Ceramic

• 50/60 @ 60%
• 60/70 @ 40%
• Diamond Concentration @ 10-12%

    D. Sintering Temperature  830-850℃